ACRYLITE
®
FF acrylic sheet is a continuously manufactured acrylic sheet. It is pro-
duced by an innovative process, resulting in a sheet offering the easy handling and
processing of extruded sheet, along with the high optical characteristics and low
stress levels expected of cast products. Colorless ACRYLITE FF sheet carries an
exclusive 10-year limited warranty on light transmission – your assurance of a
quality product. A printed copy of the warranty is available from CYRO Industries or
wherever ACRYLITE
®
acrylic sheet is sold.
The clarity and light stability of acrylic resin make it possible to manufacture
crystal clear ACRYLITE FF sheet.
ACRYLITE FF sheet is a lightweight, rigid and weather-resistant thermoplastic.
ACRYLITE FF sheet is dimensionally stable and resistant to breakage, and can be
easily sawed, machined, heat-formed and cemented.
Because of its virtually distortion-free clarity, it is well suited for use in a variety
of applications.
•
Skylights
•
Window Glazing
•
Store or P-O-P Displays
•
Signs
•
Window Frames
•
Optical Displays
•
Picture Framing
ACRYLITE FF sheet is available in thicknesses from 0.060” (1.5 mm)
to 0.944” (24 mm) and actual sheet sizes from 48” x 96” (1.22 m x 2.44 m) to
100” x 150” (2.54 m x 3.81 m). Custom sizes are also available. All sheets are
protected with polyethylene film or paper masking.
ACRYLITE FF sheet is more impact resistant than glass. If subjected to impact
beyond the limit of its resistance, it does not shatter into small slivers, but
breaks into comparatively large pieces. ACRYLITE FF sheet meets the
requirements of ANSI Z97.1 for use as a Safety Glazing Material in Buildings
(for thicknesses 0.080” to 0.500” [2.0 mm - 12.0 mm]).
ACRYLITE FF sheet will withstand exposure to blazing sun, extreme cold,
sudden temperature changes, salt water spray, etc. It will not deteriorate after
many years of service because of the inherent stability of acrylic resins.
ACRYLITE FF sheet has been widely accepted for use in school buildings,
industrial plants and outdoor signs.
Although ACRYLITE FF sheet will expand and contract due to changes in
temperature and humidity, it will not shrink with age. Some shrinkage occurs
when ACRYLITE FF sheet is heated to forming temperature, but post-forming
stability is excellent.
ACRYLITE FF sheet is only half the weight of glass and 43% the weight of
aluminum.
ACRYLITE FF sheet is not as rigid as glass or metals. However, it is more rigid
than many other plastics such as acetates, polycarbonates or vinyls. Under
wind load an acrylic sheet will bow and foreshorten as a result of deflection.
For glazing installations the maximum wind load and the size of the window
must be considered when the thickness of a panel is to be determined.
If ACRYLITE FF sheet is formed into corrugated or domed shapes, rigidity
will be increased and deflection minimized.
Large, flat ACRYLITE FF sheet, if insufficiently supported, may deform
permanently due to continuous loads such as snow, or even their own weight.
Increased rigidity obtained by forming will minimize cold flow.
Although the tensile strength of ACRYLITE FF sheet is 10,000 psi (69 Mpa) at
room temperature (ASTM D 638), stress crazing can be caused by continuous
loads below this value. For glazing applications, continuously imposed design loads
should not exceed 750 psi (5.2 Mpa) at 73°F (23°C). Temporary loads of up to
1,500 psi (10.4 Mpa) may be imposed for short durations of time at 73°F (23°C).
Characteristics
Availability
Safety
Weather
Resistance
Dimensional
Stability
Light Weight
Rigidity
Cold Flow
Strength and
Stresses
2
Localized, concentrated stresses must be avoided. For this reason, and
because of thermal expansion and contraction, large sheets should never be
fastened with bolts, but should always be installed in frames.
All thermoplastic materials, including ACRYLITE FF sheet, will gradually lose
tensile strength as the temperature approaches the maximum recommended
for continuous service–160°F (71°C).
Like most other plastics, ACRYLITE FF sheet will expand and contract from
3 to 8 times as much as glass or metals. The designer should be aware of its
coefficient of expansion and make appropriate provisions. A 48” panel will
expand and contract approximately .002” for each degree fahrenheit change in
temperature. In outdoor use, where summer and winter temperatures differ as
much as 100°F, a 48” sheet will expand and contract approximately 3/16”. Sash
rabbets must be of sufficient depth to allow for expansion as well as
for contraction.
ACRYLITE FF sheet also absorbs water when exposed to high relative humidi-
ties, resulting in expansion of the sheet. At relative humidities of 100%, 80%,
and 60%, the dimensional changes are 0.6%, 0.3% and 0.2%, respectively.
ACRYLITE FF sheet can be used at temperatures from -30°F (-34°C) up to
+190°F (+88°C), depending on the application. It is recommended that
temperatures not exceed 160°F (71°C) for continuous service, or 190°F (88°C)
for short, intermittent use. Components made of ACRYLITE FF sheet should not
be exposed to high heat sources such as high wattage incandescent lamps,
unless the finished product is ventilated to permit the dissipation of heat.
Clear, colorless ACRYLITE FF sheet has a light transmittance of 92%. It is
warranted not to lose more than 3% of its light-transmitting ability in a 10-year
period. Contact CYRO Industries for the complete warranty.
ACRYLITE
®
OP-3 acrylic sheet is formulated with ultraviolet absorbers designed
to help protect pictures, photographs and posters from the damaging effects of
ultraviolet light. ACRYLITE OP-3 sheet absorbs more than 98% of the radiation
in the ultraviolet range below 400 nanometers.
Transparent colored ACRYLITE FF sheet can be used to reduce glare and
solar energy transmittance. Transparent colored sheets are available in a range
of color densities.
This wide range of transmittance values enables the architect to select a density
which will provide adequate daylight and at the same time will control glare and
solar heat build-up.
Expansion
and Contraction
Heat
Resistance
Light Transmission
Solar
Energy
Control
Distribution
of Solar Energy
3
TOTAL
SOLAR
ENERGY
TRANSMITTED
SOLAR
ENERGY
INWARD
DISSIPATION
REFLECTED
ABSORBED
OUTWARD DISSIPATION
ACRYLITE FF sheet has excellent resistance to many chemicals including:
• solutions of inorganic alkalies such as ammonia
• dilute acids such as sulfuric acid up to a concentration of 30%
• aliphatic hydrocarbons such as hexane and VM&P naphtha
ACRYLITE FF sheet is not attacked by most foods, and foods are not affected by it.
It is attacked, in varying degrees, by:
• aromatic solvents such as benzene and toluene
• chlorinated hydrocarbons such as methylene chloride and carbon tetrachloride
• ethyl and methyl alcohols
• some organic acids such as acetic acid
• lacquer thinners, esters, ketones and ethers
For a listing of the resistance of ACRYLITE FF sheet to more than
60 chemicals, refer to the table on page 7.
ACRYLITE FF sheet will soften as the temperature is increased above 195°F
(91°C). As the temperature is increased the sheet passes through the
thermoelastic state to the thermoplastic state. The change is gradual rather than
sharply defined. The forming temperature range is between 290°F and 320°F
(143°C and 160°C). Because the sheet gradually becomes thermoplastic,
certain procedures should be considered during thermoforming. If the sheet is
to be hung in an oven it is necessary to use a continuous clamp rather than
several individual clamps. This will prevent the sheet from permanently
deforming between clamps. If the sheet is to be heated by infrared heaters
while clamped in a horizontal frame, it may be necessary to control the heaters
above the center of the sheet. This will prevent the center from becoming too
hot and sagging under its own weight.
The sheet will exhibit very little “memory” after forming and probably will not
return to its original flat condition if reheated.
ACRYLITE FF sheet will shrink in the machine direction when heated without a
frame. Sheet thicknesses of .118” (3.0 mm) and greater will shrink no more
than 3%. Thinner thicknesses could shrink more.
ACRYLITE FF sheet can be sawed with circular saws or band saws. It can be
drilled, routed, filed and machined much like wood or brass with a slight modifica-
tion of tools. Because the sheet softens quickly, it is necessary to keep the
cutting tool and machined edge of the sheet as cool as possible. Cooling of the
cutting tool is recommended. Tool sharpness and “trueness” are essential to prevent
gumming, heat buildup and stresses in the part. Heat buildup at the machined edge
could lead to subsequent stress crazing and therefore must be avoided.
Laser technology is rapidly being accepted by the industry for quick and
accurate cutting, welding, drilling, scribing and engraving of plastics.
CO
2
lasers focus a large amount of light energy on a very small area which is
extremely effective for cutting complex shapes in acrylic sheet. The laser
beam produces a narrow kerf in the plastic allowing for close nesting of parts
and minimal waste. CO
2
lasers vaporize the acrylic as they advance resulting
in a clean polished edge but with high stress levels; annealing acrylic sheet
after laser cutting is recommended to minimize the chance of crazing during
the service life of the part.
ACRYLITE FF sheet can be cemented using common solvent cements or poly-
merizable cements. The most critical factor is good edge preparation of the part to be
cemented. The edge of the sheet must be properly machined in order to have a square
flat surface and no stresses. Annealing of the part prior to cementing is recommended.
Cement and cement fumes should not contact formed or polished surfaces.
ACRYLITE FF sheet may be annealed at 180°F (82°C) with the heating and
cooling times determined by the sheet thickness. An approximate guideline is
annealing time in hours equals the sheet thickness in millimeters and the cooldown
period is a minimum of 2 hours ending when sheet temperature falls below 140°F. For
example, 1/8” (3 mm) ACRYLITE FF sheet would be heated for 3 hours at 180°F (82°C)
and slowly cooled for 3 hours.
Chemical
Resistance
Formability
Cutting
and Machining
Laser Cutting
Cementing
Annealing
4
ACRYLITE FF sheet is a combustible thermoplastic. Precautions should be
taken to protect this material from flames and high heat sources. ACRYLITE FF
sheet usually burns rapidly to completion if not extinguished. The products of
combustion, if sufficient air is present, are carbon dioxide and water. However,
in many fires sufficient air will not be available and toxic carbon monoxide will be
formed, as it will when other common combustible materials are burned. We urge
good judgement in the use of this versatile material and recommend that building
codes be followed carefully to assure it is used properly.
The combustibility test data for ACRYLITE FF sheet is: self-ignition temperature
(ASTM D-1929) is 850°F (455°C), smoke density as measured by ASTM D-2843 is
6.4%, and the rate of burning as measured by ASTM D-635 is 1.0 in/min (25mm/min)
for 1/8” (3mm) thick sheet. While these data are based on small scale laboratory tests
frequently referenced in various building codes, these tests do not duplicate actual
fire conditions.
The thermal conductivity of a material–its ability to conduct heat–is
called k-Factor. The k-Factor is an inherent property of the material, and is
independent of its thickness and of the surroundings to which it is exposed.
The k-Factor of ACRYLITE FF sheet is:
1.3 B.T.U.
or 0.19 W
(hour) (sq. ft.) (°F/inch)
m. K
Whereas the k-Factor is a physical property of the material, the U-Factor—or
overall coefficient of heat transfer—is the value used to calculate the total heat
loss or gain through a window.
The U-Factor is the amount of heat per unit time and area which will pass
through a specific thickness and configuration of material per degree of
temperature difference on each of its two sides.
This value takes into account the thickness of the sheet, whether the sheet is in
a horizontal or vertical position, as well as the wind velocity.
U-Factors are based on specific conditions (e.g., single-glazed or double-
glazed installations) and are different for summer and winter.
Listed below are U-Factors for several thicknesses of ACRYLITE FF sheet for
single-glazed, vertical installations, based on the standard ASHRAE* summer
and winter design conditions.
U-Factors–BTU/hour sq. ft. °F (w/m
2
• K)
ACRYLITE FF
Summer
Winter
Sheet Thickness
Conditions
Conditions
.118 (3.0 mm)
0.98 (5.56)
1.06 (6.02)
.177 (4.5 mm)
0.94 (5.34)
1.02 (5.79)
.236 (6.0 mm)
0.90 (5.11)
0.97 (5.51)
.375 (9.5 mm)
0.83 (4.71)
0.89 (5.05)
*American Society of Heating, Refrigerating and Air-Conditioning Engineers
The total heat loss or gain through a window (due to temperature difference
only) can be calculated by multiplying the area of the window, times the
difference between indoor and outdoor temperatures, times the appropriate
U-Factor (from Table above). Heat intake through solar radiation must be
added to arrive at the total heat gain.
ACRYLITE FF sheet is a better insulator than glass. Its U-Factor or overall
coefficient of heat transfer is approximately 10% lower than that of glass of the
same thickness. Conversely, its RT-Factor is about 10% greater.
ACRYLITE FF sheet is more resistant than glass to thermal shock and to stresses
caused by substantial temperature differences between a sunlit and a shaded area
of a window or by temperature differences between opposite surfaces of a window.
The surface of plastic is not as hard as that of glass. Therefore, reasonable care
should be exercised in handling and cleaning ACRYLITE FF sheet.
ACRYLITE FF sheet has many desirable electrical properties. It is a
good insulator. Its surface resistivity is higher than that of most plastics.
Continuous outdoor exposure has little effect on its electrical properties.
Flammability
Thermal
Conductivity
Thermal Shock
and Stresses
Surface Hardness
Electrical
Properties
5
ASTM
Typical Value
Property
(a)
Method
(0.250” Thickness)
(b)
Mechanical
Specific Gravity
D 792
1.19
Tensile Strength
D 638
10,000 psi (69 M Pa)
Elongation, Rupture
4.5%
Modulus of Elasticity
400,000 psi (2800 M Pa)
Flexural Strength
D 790
17,000 psi (117 M Pa)
Modulus of Elasticity
480,000 psi (3300 M Pa)
Compressive Strength (Yield)
D 695
17,000 psi (117 M Pa)
Impact Strength
0.4 ft. lbs/in. of notch
Izod Milled Notch
D 256
(21.6 J/m of notch)
Rockwell Hardness
D 785
M-93
Barcol Hardness
D 2583
48
Optical
Refractive Index
D 542
1.49
Light Transmission, Total
D 1003
92%
Thermal
Forming Temperature
—
Approx. 300°F (149°C)
Deflection Temperature
under load, 264 psi
D 648
195°F (91°C)
Vicat Softening Point
D 1525
220°F (105°C)
Maximum Recommended Continuous
Service Temperature
—
160°F(c) (71°C)
Coefficient of Linear
0.000040 in/in - °F
Thermal Expansion
D 696
(0.000072 m/m - °C)
Coefficient of
1.3 BTU/(Hr) (Sq. Ft.) (°F / in.)
Thermal Conductivity
Cenco-Fitch
(0.19 w/m•K)
Flammability, Burning Rate
1.0 in/min.
(0.125” thickness)
D 635
(25 mm/min.)
Self Ignition Temperature
D 1929
850°F(455°C)
Specific Heat @ 77°F
0.35 BTU/(Ib.) (°F)
(1470J/Kg•K)
Smoke Density Rating
D 2843
4.8%
Electrical
Dielectric Strength
Short Time (0.125”)
D 149
430 volts/mil (17 KV/mm)
Dielectric Constant
60 Hertz
D 150
3.6
1000 Hertz
3.3
1000000 Hertz
2.8
Dissipation Factor
60 Hertz
D 150
0.06
1000 Hertz
0.04
1000000 Hertz
0.02
Volume Resistivity
D 257
10
16
ohm-cm
Surface Resistivity
D 257
10
15
ohms
Water Absorption
24 hrs @ 73°F
D 570
0.2%
Odor
—
None
Taste
—
None
NOTES:
(a) Typical values; should not be used for specification purposes.
(b) Values shown are for 0.250” thickness. Some values will change
with thickness or pigmentation.
(c) It is recommended that temperatures not exceed 160°F
for continuous service, or 190°F for short intermittent use.
Physical Properties of
6
The table below gives an indication of the chemical
several ways. The methods of fabrication and/or
resistance of ACRYLITE FF sheet. The code used to
conditions of exposure of ACRYLITE FF sheet, as well
describe chemical resistance is as follows:
as the manner in which the chemicals are applied,
R = Resistant
can influence the final results even for “R” coded
ACRYLITE FF sheet withstands this substance for
chemicals. Some of these factors are listed below.
long periods and at temperatures up to 120°F (49°C).
Fabrication
— Stress generated while sawing,
LR = Limited Resistance
sanding, machining, drilling, and/or forming.
ACRYLITE FF sheet only resists the action of this
Exposure
— Length of exposure, stresses induced
substances for short periods at room temperatures.
during the life of the product due to various loads,
The resistance for a particular application must be
changes in temperatures, etc.
determined.
Application of Chemicals
— by contact, rubbing,
N = Not Resistant
wiping, spraying, etc.
ACRYLITE FF sheet is not resistant to this substance.
The table should therefore be used as only a
It is either swelled, attacked, dissolved or damaged
general guide and, in case of doubt, it should
in some manner.
be supplemented by tests made under actual
Plastic materials can be attacked by chemicals in
working conditions.
Chemical
Code
Chemical
Code
Acetic Acid (5%)
LR
Hydrogen Peroxide (<40%)
R
Acetic Acid (Glacial)
N
Hydrogen Peroxide (>40%)
LR
Acetone
N
Isopropyl Alcohol
LR
Ammonium Chloride
R
Kerosene
R
Ammonium Hydroxide (10%)
R
Lacquer Thinner
N
Ammonium Hydroxide (Conc.)
R
Methyl Alcohol (30%)
LR
Aniline
N
Methyl Alcohol (100%)
N
Battery Acid
R
Methyl Ethyl Ketone (MEK)
N
Benzene
N
Methylene Chloride
N
Butyl Acetate
N
Mineral Oil
R
Calcium Chloride (Sat.)
R
Nitric Acid (10%)
R
Calcium Hypochlorite
R
Nitric Acid (40%)
LR
Carbon Tetrachloride
N
Nitric Acid (Conc.)
N
Chloroform
N
Oleic Acid
R
Chromic Acid
LR
Olive Oil
R
Citric Acid (20%)
R
Phenol Solution (5%)
N
Cottonseed Oil (Edible)
R
Soap Solution (Mild dish soap)
R
Detergent Solution (Heavy Duty)
R
Sodium Carbonate (2%)
R
Diesel Oil
R
Sodium Carbonate (20%)
R
Diethyl Ether
N
Sodium Chloride (10%)
R
Dimethyl Formamide
N
Sodium Hydroxide (1 %)
R
Dioctyl Phthalate
N
Sodium Hydroxide (10%)
R
Ethyl Acetate
N
Sodium Hydroxide (60%)
R
Ethyl Alcohol (30%)
LR
Sodium Hypochlorite (5%)
R
Ethyl Alcohol (95%)
N
Sulfuric Acid (3%)
R
Ethylene Dichloride
N
Sulfuric Acid (30%)
R
Ethylene Glycol
R
Sulfuric Acid (Conc.)
N
Gasoline
LR
Toluene
N
Glycerine
R
Transformer Oil
R
Heptane
R
Trichloroethylene
N
Hexane
R
Turpentine
R
Hydrochloric Acid
R
Water
R
Hydrofluoric Acid (25%)
N
Xylene
N
Chemical Resistance of
7
Important Notice:
The information and statements herein are believed to
be reliable but are not to be construed as a warranty or representation for
which CYRO assumes legal responsibility. Users should undertake
sufficient verification and testing to determine the suitability for their own
particular purpose of any information or products referred to herein. NO
WARRANTY OF FITNESS FOR A PARTICULAR PURPOSE IS MADE.
Nothing herein is to be taken as permission, inducement or
recommendation to practice any patented invention without a license.
For the name of a local Authorized Distributor visit www.cyro.com,
or
call 800-631-5384
Visit the TechKnowlogy Center at www.cyro.com.
Visitors have immediate access to frequently asked
questions, technical information, fabrication tips,
physical properties, and hundreds of other facts
about acrylics from North America’s leading acrylic
sheet manufacturer.
www.cyro.com
CYRO Industries,
Parsippany
, New Jersey 07
054
© 2001 CYRO Industries.